ZH 510 L
PP HOMO POLYMER
ZH 510 L
RECOMMENDED USE:
Manufacture of plastic products by injection molding, extrusion or other conversion processes.
TRANSPORT:
- Ground and seal the containers while transferring the material.
- Provide adequate ventilation when used in processing conditions.
STORAGE:
- Store away from strong
- oxidizing agents.
- Protect from heat and direct sunlight.
- Store under cool, dry conditions.
- Minimize dust accumulation.
- Take precautions against
- static electricity discharges.
- Open flames are prohibited.
Share on facebook
Share on twitter
Share on linkedin
TDS
PP HOMO POLYMER
To order this product, proceed from the order registration link or contact us at the contact numbers.
FOR ORDER
| PROPERTY | TEST METHOD | UNIT | VALUE |
| Mass density (23 C) | ISO 1183 | g/cm3 | 0.945 |
| Melt Flow Rate (190 C/5.0kg) | ISO 1133 | g/10min | 0.45 |
| Melt Flow Rate (190 C/21.16 kg) | ISO 1133 | g/10min | 12 |
| FRR(21.6/5) | – | 27 | |
| Stress at Yield | ISO 527 | Mpa | 22 |
| Flextural Creep Modulus (4point,1min) | DIN 19537-2 | Mpa | 950 |
| Tensile Modulus(23 C,v=1mm/min,secant) | ISO 527 | Mpa | 850 |
| Stress at Break | ISO 527 | Mpa | 35 |
| Elongation at Break | ISO 527 | % | >850 |
| Elongation at Yield | ISO 527 | % | 8 |
| Softening Temperature | ISO 306 | C | 67 |
| Brittle Temperature | ASTM D746-72 | C | <-80 |
| shore D hardness | ISO 868 | 60 | |
| ESCR in full notch creep te2 (80 C,2%Arcopal) | ISO CD 16770 h@4.0Mpa | 50 | |
| Impact 2rength (23 C) | ISO 179/1eA | Kj/m2 | 23 |
| S4 Te2 (RCP) | ISO DIS 13477 | bar | PC >3 |
| Notch Te2 (SCG) | ISO DIS 13479 | Mpah@4.0 | >250 |
| Hydro2atic 2rength te2 (80 C) | ISO 1167 | Mpah@4.6 | >1000 |
| VN | – | Cm3/g | 300 |