2101TN47
LDPE
2101TN47
Product Description:
Low Density Poly Ethylene for Blown Film.
Typical applications:
Due to its good processability. The grade has a low energy consumption during processing and has a good draw down ability.This grade enables high speed production of film without blocking.The material is very suitable for thin industrial film,thin packaging film and carrier bags which require high toughness in combination with high resistance to tearing ,good optical properties and excellent converting properties.
Share on facebook
Share on twitter
Share on linkedin
TDS
LDPE
To order this product, proceed from the order registration link or contact us at the contact numbers.
FOR ORDER
| PROPERTIES | TEST METHOD | UNIT | VALUE |
| Polymer Properties | |||
| Melt Flow Rate | dg/min | 0.85 | |
| Density | kg/m3 | 921 | |
| Formulation | |||
| Slip | Ppm | 700 O | |
| Anti Block | Ppm | 1100 | |
| Optical Properties | |||
| Gloss (45˚) | ASTM D 2457 | % | 49 |
| Haze | ASTM D 1003A | % | 11 |
| Clarity | SABTEC method | mV | 37 |
| Mechanical Properties | |||
| Impact strength | ASTM D 4272 | kJ/m | 30 |
| Tear strength TD | kN/m | 30 | |
| Tear strength MD | kN/m | 40 | |
| Tensile test | |||
| Yield stress TD | MPa | 11 | |
| Yield Stress MD | MPa | 12 | |
| Tensile Stress at break TD | MPa | 21 | |
| Tensile Stress at break MD | MPa | 24 | |
| Strain at break TD | % | >500 | |
| Strain at break MD | % | >200 | |
| Modulus of elasticity TD | MPa | 170 | |
| Modulus of elasticity MD | MPa | 160 | |
| Coefficient of friction | ASTM D 1894 | 0,1 | |
| Blocking | g | 10 | |
| Re-Blocking | g | 30 |