HDPE BLOW MOULDING HF 4760 (BL3)
HDPE BLOW MOULDING
HF-4760(BL3)
HDPE made via Hostalen Process
HF-4760(BL3) is a blow molding grade resin with high density polyethylenee with 1-Butene as co monomer which is manufactured by the suspension polymerization of ethylene monomer. Stiffness, good ESCR are it’s spetial properties. High rigidity and good flowablity which made it proper for usage in bottles and small blow molding goods.
Features
- High density and Stiffness, good
- flowabilitty and impact Strength
- and good Stress Cracking resistance.
Applications
- Small blow moulding
- Bottles
- Containers (up to 5 lit )
- Packing of pharmaceuticals & surfactants
Additives
- Antioxidant/Process stabilizer
- Lubricant/ acid scavenger
Share on facebook
Share on twitter
Share on linkedin
TDS
HDPE BLOW MOULDING
To order this product, proceed from the order registration link or contact us at the contact numbers.
FOR ORDER
| PROPERTY | TEST METHOD | UNIT | VALUE |
| Mass density 23°C | ISO 1183 | g/cm3 | 0.954 |
| Melt flow rate (190°C/5.0kg) | ISO 1133 | g/10min | 1.2 |
| Melt flow rate (190°C/21.6kg) | ISO 1133 | g/10min | 23 |
| Stress at yield | ISO 527 | MPa | 26 |
| Flexural creep modulus(4point.1min) | DIN 19537-2 | MPa | 1300 |
| Tensile modulus(23°C.v=1mm/min.secant) | ISO 527 | MPa | 1250 |
| Stress at break | ISO 527 | MPa | 32 |
| Elongation at break | ISO 527 | % | >600 |
| Elongation at yield | ISO 527 | % | 10 |
| Softening temperature | ISO 306 | °C | 77 |
| Brittle temperature | ASTM D746-72 | °C | <-80 |
| Shore D hardness | ISO 868 | – | 62 |
| ESCR in full notch creep test (80°C.2%arcopal) | ISO CD 16770 | h @ 3.5MPa | 5 |
| Impact strength 23°C | ISO 179/1Ea | Kj/m2 | 10 |
| Swell ratio | internal | 0% | 120 |