LF 2119
LDPE
LF 2119
Product Description
LFI2119 is a low density polyethylene, with excellent optical properties. This grade offers a high output and excellent draw down and specially designed for general purpose thin films.
Typical Application
LFI2119 is recommended for blown film extrusion. This product is suitable for manufacture of general purpose LDPE film packaging and general lamination films.
General Information
Licensor: LFI2119 has been manufactured using SABTEC licensed technology.
Share on facebook
Share on twitter
Share on linkedin
TDS
LDPE
To order this product, proceed from the order registration link or contact us at the contact numbers.
FOR ORDER
| Typical Properties | Typical Value 1 | Unit | Test Method |
| Physical | |||
| MFI (190 °C /2.16 Kg) | 1.9 | dg/min | ISO 1133 |
| Density 2 | 921 | Kg/m3 | ISO 1183 (A) |
| Mechanical 3 | |||
| Impact Strength | 26 | kJ/m | ASTM D4272 |
| Tear Strength (TD) | 25 | kN/m | ISO 6383-2 |
| Tear Strength (MD) | 60 | kN/m | ISO 6383-2 |
| Yield Stress (TD) | 11 | MPa | ISO 527-1,3 |
| Yield Stress (MD) | 13 | MPa | ISO 527-1,3 |
| Tensile Stress at Break (TD) | 20 | MPa | ISO 527-1,3 |
| Tensile Stress at Break (MD) | 35 | MPa | ISO 527-1,3 |
| Strain at Break (TD) | > 500 | % | ISO 527-1,3 |
| Strain at Break (MD) | > 150 | % | ISO 527-1,3 |
| Modulus of Elasticity (TD) | 200 | MPa | ISO 527-1,3 |
| Modulus of Elasticity (MD) | 190 | MPa | ISO 527-1,3 |
| Coefficient of Friction | >1 | – | ASTM D1894 |
| Blocking | 20 | g | ASTM D3354 |
| Re-blocking | 100 | g | SABTEC method |
| Optical | |||
| Haze | 9 | % | ASTM D1003 A |
| Gloss (45°) | 55 | GU | ASTM D2457 |
| Recommended Process Conditions 4 | |||
| Extruder temperature profile: 165-185°C | Blow up ratio: 2-3 | – | — |
| film thickness: 20-50 μm | – | – | |