2004TX37
LDPE
2004TX37 (2004TC37)
Product Description:
Low Density Poly Ethylene for Blown Film.
Typical applications:
The material is intended for very thin film requiring very good optical properties and is thus mainly applied in general packaging film such as textile packaging.
Additives:
Anti oxidant – Anti block – Slip agent.
Share on facebook
Share on twitter
Share on linkedin
TDS
LDPE
To order this product, proceed from the order registration link or contact us at the contact numbers.
FOR ORDER
| Properties | Value | Unit | Test Method |
| Polymer Properties | |||
| Melt Flow Rate | 4.7 | dg/min | – |
| Density | 921 | kg/m3 | – |
| Formulation | |||
| Slip | 900 O | ppm | – |
| Anti block | 800 | ppm | – |
| Optical Properties | |||
| Gloss (45˚) | 53 | % | ASTM D 2457 |
| Haze | 9.5 | % | ASTM D 1003A |
| Clarity | 23 | mV | SABTEC method |
| Mechanical Properties | |||
| Impact strength | 15 | kJ/m | ASTM D 4272 |
| Tear strength TD | 30 | kN/m | – |
| Tear strength MD | 80 | kN/m | – |
| Tensile test | |||
| Yield stress TD | 11 | MPa | – |
| Yield Stress MD | 12 | MPa | – |
| Tensile Stress at break TD | 15 | MPa | – |
| Tensile Stress at break MD | 27 | MPa | – |
| Strain at break TD | >450 | % | – |
| Strain at break MD | 100 | % | – |
| Modulus of elasticity TD | 190 | MPa | – |
| Modulus of elasticity MD | 190 | MPa | – |
| Coefficient of friction | 0,2 | – | ASTM D 1894 |
| Blocking | < 5 | g | – |
| Re-Blocking | 100 g | – |