CRP 100 B
HDPE PIPE
CRP 100 B
Main application & Characteristics:
ARMCRP100B are high molecular weight high density polyethylene copolymers,
developed as general purpose resin for use in pressure and non-pressure pipes.
A minimum service life of 50 years is achievable under appropriate pressure
and temperature conditions. ARMCRP100B offer excellent chemical resistance
and environmental stress crack resistance.
ARMCRP100B will provide excellent resistance to effects of ultra violet light
exposure in outdoor applications.
ARMCRP100B are suitable for use in transport of a wide range of fluids for
industrial, rural and mining applications.
Suitability for use in any application should be determined by appropriate
performance testing.
* ARMCRP100B are suitable for food contact
TDS
HDPE PIPE
To order this product, proceed from the order registration link or contact us at the contact numbers.
FOR ORDER
| PROPERTY | TEST METHOD | UNIT | VALUE |
| Mass density (23 C) | ISO 1183 | g/cm3 | 0.945 |
| Melt Flow Rate (190 C/5.0kg) | ISO 1133 | g/10min | 0.45 |
| Melt Flow Rate (190 C/21.16 kg) | ISO 1133 | g/10min | 12 |
| FRR(21.6/5) | – | 27 | |
| Stress at Yield | ISO 527 | Mpa | 22 |
| Flextural Creep Modulus (4point,1min) | DIN 19537-2 | Mpa | 950 |
| Tensile Modulus(23 C,v=1mm/min,secant) | ISO 527 | Mpa | 850 |
| Stress at Break | ISO 527 | Mpa | 35 |
| Elongation at Break | ISO 527 | % | >850 |
| Elongation at Yield | ISO 527 | % | 8 |
| Softening Temperature | ISO 306 | C | 67 |
| Brittle Temperature | ASTM D746-72 | C | <-80 |
| shore D hardness | ISO 868 | 60 | |
| ESCR in full notch creep te2 (80 C,2%Arcopal) | ISO CD 16770 h@4.0Mpa | 50 | |
| Impact 2rength (23 C) | ISO 179/1eA | Kj/m2 | 23 |
| S4 Te2 (RCP) | ISO DIS 13477 | bar | PC >3 |
| Notch Te2 (SCG) | ISO DIS 13479 | Mpah@4.0 | >250 |
| Hydro2atic 2rength te2 (80 C) | ISO 1167 | Mpah@4.6 | >1000 |
| VN | – | Cm3/g | 300 |